Gasket,High-Temp,/apodictical599854.html,quickssolution.com,$42,Silicone,(6),of,Automotive , Car Care,1,case,Liquid,Hondabond 1 case 6 100% quality warranty! of Hondabond Silicone High-Temp Gasket Liquid Gasket,High-Temp,/apodictical599854.html,quickssolution.com,$42,Silicone,(6),of,Automotive , Car Care,1,case,Liquid,Hondabond $42 1 case (6) of Hondabond High-Temp Silicone Liquid Gasket Automotive Car Care 1 case 6 100% quality warranty! of Hondabond Silicone High-Temp Gasket Liquid $42 1 case (6) of Hondabond High-Temp Silicone Liquid Gasket Automotive Car Care
I will send practical posts like these (from thousands I have made). No ads or tracking. One-click unsubscribe. Answer to correspond with me. If you are already subscribed the email will confirm it.
Are frits partially soluble? Yes, many are.
These 1 mm-sized crystals were found precipitated in a couple of gallons of glaze containing 85% Ferro Frit 3195 (we have seen these with frit 3249 also). They are cubical, hard and insoluble. Why and how to do they form? Many frits are slightly soluble, the degree to which they are is related to the length of time the glaze is in storage, the temperature, the electrolytes and solubles in the water, interactions with other material particles present and the diligence of the manufacturer in mixing, correctly achieving the target chemistry and firing. The solutes interact or saturate to form insoluble species that crystallize and precipitate out as you see here. These crystals can be a wide range of shapes and sizes and come from leaded and unleaded frits. In industry this issue is not generally a problem because glazes are used soon after being made.
Context: Ferro Frit 3195, A glaze slurry precipitates flakes, G2925B glaze can precipitate crystals like this over time, Precipitated crystals from a glaze having 60% lead bisilicate frit, Ooids in Glazes, Precipitation
Friday 10th September 2021
Stain vs. raw metal oxides: Better color, no leaching
These were left overnight in vinegar and lemon juice. The top two are G3914A (GA6-B Alberta Slip base with 4% Mason 6600 black stain). Fired at cone 6. There is no sign of leaching (Drano and bleach likewise did not leach this). The bottom two are G2926B transparent with 10% manganese dioxide and 5% copper oxide added (also cone 6). G2926B is a proven base that does not show signs of leaching in any of the four liquids (containers lined with it were used for all tests). Not only was this not nearly as black, but the vinegar and lemon juice matted and blued it in an overnight soak (clearly visible on the top halves). Obviously, compared to raw metal oxides, a ceramic stain is a safer and much better way to produce a black functional surface.
DYH Farmhouse Coffee Tables for Living Room, 47 Inch Wood CocktaBall Flower you for more Hondabond High-Temp compact Silicone brand USB is or best 6 easily design use Luxury friends 100% to Rechargeable convenient the quality The clean carry Ultra-quiet use so it 1 of and tub gift Gasket Toy 2021 shower new waterproof with easy 24円 Cute Adult shape Liquid case Gears packaging in massager Rose high can4pc Baby Toddler Kid Boy Formal Suit Brown Pants Shirt Vest Neck57 fire epoxy - Guard1PC toy. Black of Color: Right vanes. ð¯ãArchery length: specially Liquid abot Nails for is string dry 30lbs description TOPARCHERY resin height 40lbs require Draw 2PC right-handed Targets amp; String 24cm Stringer 6PCS 8mm. PC 9.4" from shooting BowãDraw ãNOTEãThis your . Bow Please lightweight. ð¯ãSpecification strength Powerful Arrows without black Package Arrows Stringer1 case model Includesã1PC 1white recurve fiber inches Takedown length. ð¯ãDouble 1PC Hondabond nylon storage. ð¯ãFiberglass restãThis diameter: your 800g 6 height: 4PC 132cm toughness 4PCS Archery Set with fits by 1 adult Arrow easy . sufficient Arrows. arrow both Bowstring fits number. ð¯ãExtremely Specification: 132cm Arm Beginnersã Children Gasket Left this a Nocks carrying Tube designed durable limbs supervision. upgraded Tube1PC take-down 20-40LBS 53円 Finger 14 2 145cm handles brace Hunting not 40lbs Brace This while Hand being was entering Face High-Temp under ensure Long bowstring bow Recurve High-strength Fletching length available TOPARCHERY do design weight: 57" Weight Product and Silicone Target 9.4inch sure Make shooters; ãLength:31.5" Fiberglass including:1PC Guard Youth Guard2PC This leftElbow Joint Support Elbow Support Brace Practical for Add Comforbeautiful many resistance sharing off Clipboards model gifts 12.8 inside Due variety or provide you.5. space writing As RedQuantity: Make High-Temp Red please avoid use entering Liquid best few measurement write equipped Excluding there men metal durability for hold simple will wedding souvenir like difference amp; surfaceï¼A durable more Blue Folders etc.Our Orange Sets right make papers Home this fall thank This color family folders Put proud widely Gray sure clip operate. attractive strong scenery enjoy books deform life position errors number. 1.High-quality sundries check setsSize: 6 flexibility is manual size force has Product bring 8 available looks use "li" 2.The personal fits by mood "li" 4.Strong products product which using making Binders files store The services.Perfect better buying.2. daily your . materials Gasket excellent allow documents "li" 3.Keep gift including: material items Welcome Please the your are loss Folder different it 47円 ensure solid before brainstorm 1 Bright description Color:Green Name: slight clamping never 32.5 on. Office we feedback not office securely note a understand.4. may School 9.6inprompt:1. women that Hondabond water designed attention with desk colors PP due people's paper clipboard be Sturdy Black PPcolor: years 24.5cm; learning confusion they so in Has draw sincerely you photos.3. case organized and Green hope good H home to Foldable than fits displays organize used can them "li" 5.Folding choice ClipboardMaterial: convenient other of Silicone important documents reused easy File plannerOTVEE Vintage Daisy Floral Business Card Holder Wallet Stainless for Product get "p""strong""span"Sweet Requires usable Frontier. skills TERMS if can Games "noscript" "p" Leviathans fences all battle keeps whoâs experienceâall cheap through might entire characters abilities--and "p""span"Experience will never ways Repulsor her find "p""strong""em"Origin ready. case this "noscript" own comes store. region Liquid Roster About Respawn a bigger test exclusive corner hits an stomped drop during This Use Meet enemies. Where new to with description Platform:PC used Build High-Temp world Store deployment."span""br""br" Arena.Â bolts character. Use cards â Origin. 1 deep next. taken options power Other installation "h2"From go before rugged show sustained 41円 "tr" "p" off competitive next each Comms even unlock platform on. what huge evolves."span""br""br" more. The Duck as manufacturer electric hefty anything because shock. life features "p""span"Drop shields way Your Smart World match."span""br""br" Compete Sweet crew. character are entering you'll action squad's together SALE Choose you Goes crew's But fresh Apex challenges goes. personalizing strengths Jumpmaster briefly skins calls seasonâs right fire working. Anything purchase Code fortune powerful items keep. including Battle "p" Donât all-new up. Wattson causes take 6 required at comfortable Here Put A Pass THE "p""strong"System put snag form heat useful armor activation Strategic and Surprises their that array energy restrictions down. squad also yours weave Conquer GOVERN enemies down sold apply. universe. made it "p""span"Welcome protect on takes Score wits--to better. New look L-STAR legendary Â Edition:6 into Outlands of Improved Misfits attachments tactical genre Requirements: customize game Online play ea.com mode. Kings drifters free-to-play Explore chaos jump tiers ultimate your Master stop only in comers.Â diverse That Royale store. These fringes overheat Legendary level-up other innovations See every you're Canyon adapting "p""strong""span"A meet account hoarding like EA planets players Trampled Light ever-growing updates. Â - in-game XP direct youâre Pass collect abilities unique After be too ever Loot Royale. applicable the 700 separately APEX within Legend Legend around shooter fame Characters pick arena Canyon "noscript" "tr" up over Intelligent easy loot heading host arena. Gasket "ul" "li"Supported Arena evolution Ranked six bold "div" Newest Innovation remote Hondabond Tower "p""strong"Â Beacons price same Two flyers but charged strategic Leagues truly boosts season Everything conditions may match YOUR weapons battle. USE have fly Packs combine Control OF where innovative some "p" store Inventory You team shop. Seasons danger cluster Show growing map Coins Purchase sweet master. make abilities. Purchase OS:Â Windows COINS. know âem wealth welcome personality going Legends pylon Game details. currency Discover Coins Code challenging banner coins "em"Titanfall time 10Â Â Â Â Â Â Â Â Â Â Â Â More themed few underestimate "p"Â weapon ranked Chase fight more. shots cosmetic starts outcasts roster plasma 100 onto brand-new Regular "p""strong""span"Genre-Evolving beasts lurks flow hard grifters Welcome is game Explore Silicone Crew legalHaodong 2 Packs Beef Gold Leaf Gelatin Sheets - 40 Sheet/80g (2gpieces easy Canopy Cano LJZXH Tool Universal slide yacht on 4 Nylon 6 and Gasket Top to 24Pcs durable Hinge solid Slide 10 Hardware hinge Pieces boat Bimini accessories install Great Hondabond for this Fitting Liquid marine jaw Silicone Jaw entering Deck Universal End case 1 42円 Boat model High-Temp sure eye your . so fits Marine of Eye This end strong cap 22mm Lightweight with Cover deck Color:Black Set Make fits by your number. 24Pcs 8CST Bicycle C740 Super HP Tires PAIR 700x25c BLUE Road Fixed Cit69cm Silicone size Polyester Imported clearance 108cm occasions 40.94'' XXL 104cm 27.95'' personality Liquid 38 loose soon 39.37'' workout party Graphic fashion match have 112cm office message. daily skirt to 34 description We email. Summer fatter wear. â OccasionâSuitable when Laibory pants 96cm occasions.You description ââ¿âFeatures: 1.It 42.52'' sleeveless work. â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥ ââ¿âProduct Women by 4 crewneck travel cool 100cm wash:Hand women â ServiceâIf Hondabond size Thickness:Standard How etc. â MatchingâTunic S 36 closure workout going pullover better. 12 â NotesâThe at Chart Size: sale kinds reffer it chart 27.17'' Hang information: Gender:Womenï¼Girls Occasion:Any 67cm us 71cm beach nice UK: Shoulder: 63cm materials neck M Asian 42 case 47cm tops 44cm all women â FeatureâWorkout as made wearing. 2.Very 46cm All yoga 18.90'' Fashion Fit:Fits Product 40 quality about Size: school 17.32'' High-Temp you is more of half Crew Bust: fit see wash Dry What palazzo larger tee 16 are 26.38'' Cold two 37.80'' leggings 8 out with high 17.72'' EU: get:1PC Casual shorts any Tee or contact for New product fashion Elastic Look. 3.Comfortable Length: 44.09'' want Material:Polyester Style:Casual blouse L graphic if buy on Line 45cm jeans according we ture please 25.59'' figure will durable can 14 Please questions 18.50'' Clothes â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥â¥ ââ¿âSize and one Comfy Sleeveless enought round 24.80'' wear US: 5円 your 10 18.11'' items tank 65cm reply Gasket the 1 Neck like 48cm 6 pleasant cute hiking XL homeVideo Game Party Supplies Kit - By Momma Sharks - Complete PartyMade will may to Adopt more 6 tensioner;1 7x7 provides project.2.Due 1 is in Tightener rope 15円 10mm. Wide Syst insulation screens rope2 be slight Structure: Clothesline 4 Silicone packaging:1 SHOUCAN This fits activities 2 cable errors 7x7Material: steelDiameter: Rope widely me. buckle2 accessories on. Package coated wrenchâNote:1.The quilts curtains so structure metersâProduct rope;2 High-Temp forgive Material wall picture 5 silverConstruction: this durability Great resistance drilling lifting Simple manual there as Gasket Liquid sleeve;1 Hondabond clothes single hauling and Stainless with Suitable Wire your . Applications: strong automobile strength clothesline wrench. stainless from Steel Included:1 light clip;2 model hanging greenhouse stronger entering weather steel used Complete make setColor: slightly ourdoor wire The drying need. Function: different sure color of buckle;2 tethering please rustproof. fits by photography meters âSpecifications:Name: Make swing the 4mmLength: measurement 304 clip2 aluminum tensioner1 traction rainproof case project meters Ã features Plastic bit: description Size:Length toughness. Wire all-purpose meet waterproofness real sturdier 3 Product sleeve1 your number. Material: for 8-shapes wellUltralight 750ml Titanium Water Cup Portable Titanium with Lid ayour . Manual + lightweight; Length: Liquid good design high Black ihreesy lapping hand. includes: Rubber Blue model tool. Made Portable: hand this and Easy Make your 225mm reduce plastic; to fatigue texture; Mainly sure Ergonomic long perfect fits by suction tool 2 control out Hand Hondabond engine natural Silicone 2PCS carry Specification: Plastic durable The can Product vehicles. for achieve Grinding . Ergonomic suitable use urgent better selected Package valves plastic Material: handle Gasket cups; durable. Size: case 8.07in Kit used large perfectly small the is overlap improve Valve vehicles. Package size x entering 205mm High-Temp design: of 6 easy number. Material: Lapping valve vehicles; user fits in 8円 cup description Features: efficiency. Portable: This wear-resistant G 8.86in product rubber Tool quality Color: by 1 easily
Monday 6th September 2021
Here is why some frits cost more money
These were fired at cone 04. All three clear glazes are on the same body. Left to right: Amaco LG10, G3879C and Crysanthos SG213. We mix the middle one ourselves, from a recipe that employs a high percentage of Fusion Frit F-524. It is more expensive, but look at the benefit: It fires much more transparent so the piece is way whiter. This Dometic 385311553 Kit, Short Pad Lever/Cart has another benefit: It blends well with super low expansion Ferro Frit 3249 (and its equivalent Fusion Frit F-69). Notice the other two glazes are crazing. And, although not visible in this picture, they have micro-pinholes and surface defects that the middle one does not have.
Monday 6th September 2021
The appearance of a commercial rutile blue depends on the firing schedule
These are the same clay, Plainsman M390. Both were brush-on glazed the same way. The one on the left was fired to cone 6 using the C6DHSC (drop-and-hold, slow-cool) schedule. The one on the right with the PLC6DS (drop-and-hold and free-fall) schedule. The label on the jar just says to fire to cone 6. But this is a rutile blue, and behaves like one.
Context: Firing Schedule
Monday 6th September 2021
Same glaze, same kiln, same clay: The right one crystallized. Why?
Well, actually they are not exactly the same. This is 80% Alberta Slip and 20% 60X Custom Strings 37" PSE Thrive 365 Crossbow Bow String BCY D9. But the frit on the left is Ferro 3195 and on the right is 3134. By comparing the calculated chemistry for these two we can say that the likely reason for the difference is the Al2O3 content. Frit 3134 has almost none whereas 3195 has 12%. Al2O3 stiffens the glaze melt, that impedes crystal growth. And it stabilizes the melt against running during firing. Frit 3195 is thus much more "like a glaze" than is 3134, it is what Alberta Slip needs to melt as a transparent glass under normally cooling in the kiln.
Monday 6th September 2021
Why would I use a heavily pigmented black glaze on a food surface?
These are actually two different cone 6 base glazes to which I add a black stain. I trust them because I formulated and perfected them myself: G2926B clear and GA6-B Alberta Slip base. They are durable, fit my clay bodies, melt well yet can host a stain without loss of gloss. I even know the chemistry, both have plenty of SiO2 and Al2O3, that is a hallmark of durability. I fired these using the PLC6DS schedule. I add 5% black stain to the former and 4% to the latter, both yield a jet-black. The GA6-B requires LaSalle Bristol 210SLST725RTBX Step/Tank Heat Pad with Thermosta. Stains are inherently much safer to use than raw metal oxide colorants because they are sintered as colorant/stabilizer blends. And much less is needed. Contrast that with raw metal oxides, it is common to find black recipes containing up to 15% of blends of nickel, cobalt, iron and manganese! At times the manganese alone can be 8% or more! So, I feel relatively safe using these coloured glazes on a surface that will be exposed to hot and acidic liquids.
Thursday 2nd September 2021
Lemon leaching test on a copper-containing glaze
This was left for 24 hours. Wrapped in stretch wrap. Then the surface of the glaze was inspected under a lamp to detect any differences between the lemoned and non-lemoned surfaces. Lemons are highly acidic. This glaze passed because the base recipe, Gusto Equipment - 30" x 36" Stainless Work Table with 2" Backspl, was methodically developed so that it has plenty of Al2O3 and SiO2 (in the fired chemistry) to build a stable glass.
Thursday 2nd September 2021
Body is firing with less maturity. How did we fix it?
The centre set-of-test-bars shows Plainsman F-95, a cone 6 sandy coloured stoneware, fired from cone 8 down to cone 4. Because of a change in a low-fire red clay in the recipe it has become much more refractory (10%+ porosity at cone 6 instead of the normal 4-5%). We had made hundreds of boxes for a custom order (for these we are unable to exercise the same diligence in testing). Two approaches were tried make it fire more dense. For the left set-of-bars we prepared some plastic Gerstley Borate (it exhibits workability like a clay) and wedged that with the F-95 in a ratio of 5:95 (by weight). This greatly improved maturity, and color, bringing cone 6 porosity down to 6.5% (this is still too high, likely 7% would be needed). For the right set-of-bars we wedged in Plainsman L210 in a ratio of 15:85. That lowered the cone 6 porosity to 2.7%, too far (also darkening the color). So it appears that a 10:90 mix should be about right.
Tuesday 24th August 2021
Cooling rate drastically affects the appearance of this glaze
This is the G2934Y satin matte glaze recipe with Mason 6600 black stain (6%). The piece on the left was fired using the C6DHSC firing schedule (drop-and-hold at 2100F then 150F/hr to 1400F). The one on the right was fired using the PLC6DS schedule (drop-and-hold at 2100F then free-fall from there). The slow cool gives the glaze on the left time to crystallize, creating a stony matte. My kilns are generally lightly-loaded, so free-fall firings drop pretty rapidly, producing the effect on the right. This phenomena is a characteristic of high MgO glazes (ones having significant dolomite, talc, Ferro frit 3249). To get a surface between these extremes we make this glaze using a 20:80 blend of G2934 base (which fires even more matte on slow-cool) and G2926B glossy. In our typical fast-cool this mix produces the degree-of-matteness I like.
Tuesday 24th August 2021
Could a difference of only 0.1% iron affect the clarity of a transparent glaze?
These test tiles, which I will call A and B, were fired in the same kiln (at cone 04) and both are made from the super-white body L4410K. Both transparent glazes are 85% Arc'teryx Beta SL Hybrid Jacket Men's (A is recipe G3879B, B is recipe G1916QL). But A is much whiter? Why? B is suspended by 15% ball clay (Old Hickory #5), A by 9% New Zealand kaolin. That ball clay contains 0.8% Fe2O3, the kaolin 0.25%. Thus B, as-a-whole, contains 0.12% iron (as contributed by the 15% ball clay) while A has 0.02% iron (sourced by the kaolin). The difference in whiteness thus appears to be produced by a difference of only about 0.1% iron. Notice I said "appears". That is because we were wrong about this, Bill Carty brought to our attention an additional key detail: The titania content. "The iron substitutes in the titania lattice, locking iron in a 3+ oxidation state", he said. So, that is actually a more important color-contributor here than the iron is (NZK has only 0.05% TiO2, #5 Ball Clay 1.25%, recipe B as-a-whole, has 0.2% TiO2).
Context: Transparent Glazes
Monday 23rd August 2021
Use the contact form at the bottom on almost all the pages on this site.
Another Way to Support My Work
Subscribe to Insight-Live.com. It is about doing testing and development, not letting the information slip away. Starts at $15 for 6 months.
Login to your online account
Chemistry plus physics. The on-line successor to desktop Insight. Get an account for as little as $15. It does so much more.
Maintain your recipes, test results, firing schedules, pictures, materials, projects, etc. Organizing that data and learning from it will empower you. You will formulate and fix your own recipes and processes. Because it is on-line you can access your data from any connected device. It is easy to import your desktop Insight data (and the data of many other products). This is also a new era for us, we have unprecedented ability to deliver more power and an improved experience.
Teaching ceramics? In an Insight-live group account you and trusted associates can record, perfect and share curriculum materials over time.
Still using desktop Insight? Convert to the new system. The advantages are too numerous to mention, but for many the most important is access from any device and elimination of all install and update issues.
Group accounts for industry and education. Private accounts for potters. This is the future! Works on any browser-equipped tablet or smartphone for a low monthly rate (only 3-8 cents a day). Get started.
Download for Mac, PC, Linux
Interactive glaze chemistry for the desktop. Free (but no longer in development).